Data analysis of the influence of microstructure, composition, and loading conditions on stress corrosion cracking behavior of Mg alloys.

Stress corrosion cracking (SCC) can be a crucial problem in applying rare earth (RE) Magnesium alloys in environments where mechanical loads and electrochemical driven degradation processes interact. It has been proven already that the SCC behavior is associated with microstructural features, compositions, loading conditions, and corrosive media, especially in-vivo. However, it is still unclear when and how mechanisms acting on multiple scales and respective system descriptors predictable contribute to SCC for the wide set of existing Mg alloys. In the present work, suitable literature data along SCC of Mg alloys has been analyzed to enable the development of a reliable SCC model for MgGd binary alloys. Pearson correlation coefficient and linear fitting are utilized to describe the contribution of selected parameters to corrosion and mechanical properties. Based on our data analysis, a parameter ranking is obtained, providing information on the SCC impact with regard to ultimate tensile strength (UTS) and fracture elongation of respective materials. According to the analyzed data, SCC susceptibility can be grouped and mapped onto Ashby type diagrams for UTS and elongation of respective base materials tested in air and in corrosive media. The analysis reveals the effect of secondary phase content as a crucial materials descriptor for our analyzed materials and enables better understanding towards SCC model development for Mg-5Gd alloy based implant.

Comparison of 2D and 3D Plasma Electrolytic Oxidation (PEO)-Based Coating Porosity Data Obtained by X-ray Tomography Rendering and a Classical Metallographic Approach.

In this work, the porosity of plasma electrolytic oxidation (PEO)-based coatings on Al- and Mg-based substrates was studied by two imaging techniques-namely, SEM and computer microtomography. Two approaches for porosity determination were chosen; relatively simple and fast SEM surface and cross-sectional imaging was compared with X-ray micro computed tomography (microCT) rendering. Differences between 2D and 3D porosity were demonstrated and explained. A more compact PEO coating was found on the Al substrate, with a lower porosity compared to Mg substrates under the same processing parameters. Furthermore, huge pore clusters were detected with microCT. Overall, 2D surface porosity calculations did not show sufficient accuracy for them to become the recommended method for the exact evaluation of the porosity of PEO coatings; microCT is a more appropriate method for porosity evaluation compared to SEM imaging. Moreover, the advantage of 3D microCT images clearly lies in the detection of closed and open porosity, which are important for coating properties.

In Situ Synchrotron Diffraction Analysis of Zn Additions on the Compression Properties of NK30.

In situ synchrotron radiation diffraction was performed during the compression of as-cast Mg-3Nd-Zn alloys with different amounts (0, 0.5, 1, and 2 wt %) of Zn addition at room temperature. During the tests, the acoustic emission signals of the samples were recorded. The results show that the addition of Zn decreased the strength of the alloys but, at the same time, increased their ductility. In the earlier stages of deformation, twin formation and basal slip were the dominant deformation mechanisms. The twins tended to grow during the entire compression stage; however, the formation of new twins dominated only at the beginning of the plastic deformation. In order to accommodate the strain levels, the alloys containing Zn underwent nonbasal slip in the later stages of deformation. This can be attributed to the presence of precipitates containing Zn in the microstructure, inhibiting twin growth.

Phase Formation during Solidification of Mg-Nd-Zn Alloys: An In Situ Synchrotron Radiation Diffraction Study.

Mg-4Nd base alloys with Zn additions of 3, 5 and 8 wt % were investigated with in situ synchrotron radiation diffraction during solidification. This method enabled the investigation of phase formation and transformation in the alloys. The diffraction results were supported with TEM observations on the as-solidified samples. The results show the effect of increased Zn addition on stabilizing the Mg3RE phase (RE-rare earth). The experimental results agree only partially with the theoretical calculations indicating the need to improve the existing thermodynamic database on the alloy system.

The Effect of Zn Content on the Mechanical Properties of Mg-4Nd-xZn Alloys (x = 0, 3, 5 and 8 wt.%).

The mechanical properties of as-cast Mg-4Nd-xZn (x = 0, 3, 5 or 8 wt.%) alloys were investigated both in situ and ex situ in as-cast and solution-treated conditions. The additions of 3 or 5 wt.% Zn in the base Mg-4Nd alloy did not improve yield strength in comparison to the binary Mg-4Nd alloy. Mechanical properties were shown to improve only with the relatively high concentration of 8 wt.% Zn to Mg-4Nd. The change in intermetallic morphology from a continuous intermetallic to a lamella-like intermetallic was the primary reason for the decreased mechanical properties in Mg-4Nd-3Zn and Mg-4Nd-5Zn compared with Mg-4Nd and Mg-4Nd-8Zn. The dissolution of intermetallic at grain boundaries following heat treatment further indicated the importance of grain boundary reinforcement as shown in both in situ and ex situ compression testing. Azimuthal angle-time plots indicated little grain rotation most noticeably in Mg-4Nd, which also indicated the influence of a strong intermetallic network along the grain boundaries.